Quantum dot sensitized wide bandgap semiconductor photovoltaic devices &amp; methods of fabricating same

ABSTRACT

A quantum dot (QD) sensitized wide bandgap (WBG) semiconductor heterojunction photovoltaic (PV) device comprises an electron conductive layer; an active photovoltaic (PV) layer adjacent the electron conductive layer; a hole conductive layer adjacent the active PV layer; and an electrode layer adjacent the hole conductive layer. The active PV layer comprises a wide bandgap (WBG) semiconductor material with E g ≧2.0 eV, in the form of a 2-dimensional matrix defining at least two open spaces, and a narrower bandgap semiconductor material with E g &lt;2.0 eV, in the form of quantum dots (QD&#39;s) filling each open space defined by the matrix of WBG semiconductor material and establishing a heterojunction therewith. The active PV layer is preferably fabricated by a co-sputter deposition process, and the QD&#39;s constitute from about 40 to about 90 vol. % of the active PV layer.

FIELD OF THE INVENTION

The present invention relates to improved quantum dot sensitized wide bandgap semiconductor photovoltaic devices and methods for fabricating same. The invention has particular utility in the manufacture and use of photovoltaic solar cells for direct conversion of radiant to electrical energy.

BACKGROUND OF THE INVENTION

A recently developed class of photovoltaic (“PV”) cells and devices, sometimes referred to as “Graetzel Cells” (see, e.g., U.S. Pat. Nos. 4,684,537; 5,350,644; 5,463,057; 5,525,440; and 6,278,056 B1), is based upon dye-sensitization of a wide bandgap (“WBG”) semiconductor (i.e., E_(g)≧2 eV, preferably ≧3 eV), such as TiO₂, for efficient injection of electrons into the conduction band upon photo-excitation of the dye molecules, followed by charge separation and photovoltage generation utilizing a liquid electrolyte for hole conduction. While such devices are attractive in terms of their inherent simplicity and use of environmentally stable WBG material, the relatively low absorption coefficients of the photodyes necessitates use of extremely thick “mesoscopic” TiO₂ films for adequate capture of incident photons. Disadvantageously, however, this results in greater opportunity for loss of excited electron-hole pairs (“excitons”) due to recombination and thermalization. Consequently, the efficiency of solar conversion of such devices is generally limited to ˜10%.

According to a variation of this approach, quantum dots (“QD's”), i.e., nano-dimensioned semiconductor particles that confine the motion of conduction band electrons, valence band holes, or pairs of conduction band electrons and valence band holes (“excitons”) in all three spatial directions, are substituted for the abovementioned dye molecules (see, e.g., U.S. Pat. Nos. 6,861,722 B2 and 7,042,029 B2). Contact between porous TiO₂ films and the QD's, may for example, be accomplished via absorption, utilizing a porous TiO₂ body and a colloidal solution of the QD, or produced via an in situ process. PV effects have been observed with a number of semiconductor-based QD's, including InP, CdSe, CdS, and PbS. Advantages of QD's vis-à-vis dye molecules in solar PV applications involving sensitization of WBG's include better tunability of optical properties via size control of the QD particles and better heterojunction formation with solid, rather than liquid hole conductors.

As explained below, another advantageous capability of QD-sensitized PV cells is the production of quantum yields >1 by impact ionization, sometimes referred to as the “inverse Auger effect”. Since the inverse Auger effect is not possible with dye-sensitized PV cells, much higher conversion efficiencies are possible with solid state heterojunction QD-sensitized PV cells.

Referring to FIG. 1, shown therein, in schematic form, is a band diagram for solid state heterojunction QD-sensitized PV cells, wherein: CB and VB respectively indicate the conduction band and valence band energies of the QD and WBG materials (illustratively PbS and TiO₂, respectively), E_(F) represents the respective Fermi energy levels, and Φ_(A) indicates the respective electron affinities (work functions). In order for charge injection (sensitization) from the QD to the WBG material to occur, the difference between the work function Φ_(A) and conduction band energy CB must be greater for the WBG than for the QD.

Design rules for the materials selection process for fabricating solid state heterojunction QD-sensitized PV cells such as shown in FIG. 1 include:

-   -   1. the minimum size of the QD, i.e.,         D_(min)=(πh)/2m_(e)*ΔE_(c))^(1/2), where m_(e)* is the effective         mass of the electron, and ΔE_(c) is the difference between the         energies of the CB's of the QD and WBG materials, wherein the         bandgap energy E_(g) of the WBG semiconductor material is ≧2.0         eV, preferably ≧3.0 eV; and the bandgap energy E_(g) of the QD         semiconductor material is <2.0 eV, preferably <1.0 eV; and     -   2. the exciton radius, a_(x), is larger than the QD radius,         where a_(x)=ε₁/M*a_(H), wherein is the relative permittivity and         M*=(M_(e)*M_(h)*)/(M_(e)*+M_(h)*) and M_(e)* and M_(h)* denote         the effective masses of the electrons and holes in units of the         electron rest mass and a_(H) is the Bohr radius of 5.29×10⁻¹¹ m.         The QD radius D_(min) ranges from about 3 to about 15 nm, and is         typically about 5-9 nm.

The term “exciton radius” a_(x) refers to the average physical separation between the electron and hole of the electron-hole pair within the semiconductor. If the size of the semiconductor particle, i.e., QD, is less than or equal to the exciton radius, quantum confinement occurs and the energy levels in the QD are discrete and continuous energy level bands are no longer formed. Typical values of ax range between about 2 and about 20 nm.

Adverting to FIG. 2, schematically illustrated therein is a band diagram for describing the increase in photon conversion efficiency afforded by QD's, wherein enhanced photocurrent is obtained when energetic (“hot”) charge carriers (e⁻h⁺ pairs or excitons) produce a second (or even a third, etc.) e⁻h⁺ pair or exciton via impact ionization, a process which is the inverse of an Auger recombination process wherein two e⁻h⁺ pairs recombine to form a single, highly energetic e⁻h⁺ pair. In order for the inverse Auger recombination process to result in increased photon conversion efficiency, the rate at which impact ionization occurs must be greater than the rate of carrier “cooling” and other relaxation processes for hot carriers.

Referring now to FIG. 3, schematically illustrated therein is a band diagram illustrating the mechanism of operation of a solid state heterojunction QD-sensitized PV cell comprising a layer of a WBG semiconductor material (i.e., E_(g)≧2.0 eV, preferably ≧3.0 eV), e.g., TiO₂, forming a heterojunction with a layer of a narrower bandgap QD semiconductor material (i.e., E_(g)<2.0 eV, preferably <1.0 eV), e.g., PbS. The latter is contacted at an opposite interface with a hole conductor, e.g., a layer of a hole conductive semiconductor material. Respective contacts (output terminals) are formed on the TiO₂ and hole conductive semiconductor layers for obtaining an electrical output from the cell for supply to a load device. As shown in the figure, absorption of a photon in the QD results in formation of an energetic e⁻h⁺ pair (or exciton) in the QD, which e⁻h⁺ pair (or exciton) then produces a second e⁻h⁺ pair in the QD via impact ionization. Both excited electrons in the conduction band of the QD may then be efficiently transferred to the conduction band of the electron conductive WBG semiconductor, and thence to the negative output terminal. Hole transport occurs in the opposite direction via the valence bands of the QD and hole conductive semiconductor to the positive output terminal. FIGS. 4(A) and 4(B) schematically illustrate the directions of electron and hole travel, respectively, in the QD-sensitized PV cell of FIG. 3. As shown in FIG. 4(A), if any portion of the QD is in interfacial contact with the negative output terminal, excited electrons present in the QD may also travel directly to the negative output terminal to produce photocurrent.

Notwithstanding the potential for increased photon conversion efficiency afforded by the solid state heterojunction QD-sensitized PV cells such as described above, the heretofore utilized manufacturing techniques comprising absorption of the QD material from solution onto a porous body of a WBG semiconductor material, as well as in situ processing, result in relatively low surface-to-volume ratios of the WBG semiconductor particles (e.g., TiO₂), which when combined with the relatively low coverage of the WBG particle surfaces with QD's, limits the actual performance and viability of such devices.

Accordingly, there exists a clear need for improved solid state heterojunction QD-sensitized PV cells capable of performing in optimal manner at high solar photon conversion efficiencies. Further, there exists a clear need for improved methodology for fabrication of such improved solid state heterojunction QD-sensitized PV cells in cost-effective manner utilizing readily available manufacturing instrumentalities and technologies.

DISCLOSURE OF THE INVENTION

An advantage of the present invention is an improved quantum dot (QD) sensitized wide bandgap (WBG) semiconductor heterojunction photovoltaic (PV) device.

Another advantage of the present invention is an improved quantum dot (QD) sensitized wide bandgap (WBG) semiconductor heterojunction photovoltaic (PV) device with an active PV layer having a substantially increased QD content.

Still another advantage of the present invention is an improved quantum dot (QD) sensitized wide bandgap (WBG) semiconductor heterojunction photovoltaic (PV) device with dual-sided irradiation capability.

Yet another advantage of the present invention is an improved method of fabricating quantum dot (QD) sensitized wide bandgap (WBG) semiconductor heterojunction photovoltaic (PV) devices.

A further advantage of the present invention is an improved method of fabricating quantum dot (QD) sensitized wide bandgap (WBG) semiconductor heterojunction photovoltaic (PV) devices with active PV layers having substantially increased QD content.

A still further advantage of the present invention is an improved method of fabricating quantum dot (QD) sensitized wide bandgap (WBG) semiconductor heterojunction photovoltaic (PV) devices with dual-sided irradiation capability.

These and additional advantages and other features of the present invention will be set forth in the description which follows and in part will become apparent to those having ordinary skill in the art upon examination of the following or may be learned from the practice of the present invention. The advantages of the present invention may be realized as particularly pointed out in the appended claims.

According to an aspect of the present invention, the foregoing and other advantages are obtained in part by an improved quantum dot (QD) sensitized wide bandgap (WBG) semiconductor heterojunction photovoltaic (PV) device, comprising:

a wide bandgap (WBG) semiconductor material with E_(g)≧2.0 eV, in the form of a 2-dimensional matrix defining at least two open spaces; and

a narrower bandgap semiconductor material with E_(g)<2.0 eV, in the form of quantum dots (QD's) filling the open spaces defined by the matrix of WBG semiconductor material and establishing a heterojunction therewith.

In accordance with embodiments of the present invention, the device further comprises an electron conductive layer adjacent a first side of the active PV layer; a hole conductive layer adjacent a second side of the active PV layer; and an electrode layer adjacent the hole conductive layer. Each QD is columnar- or grain-shaped and extends from the electron conductive layer to the hole conductive layer; the WBG and narrower bandgap semiconductor materials are immiscible; each QD is isolated by the matrix of WBG semiconductor material; the WBG semiconductor material has a bandgap E_(g)>3.0 eV and is an electron conductive material selected from the group consisting of: TiO₂, ZnS, ZnO, Ta₂O₅, Nb₂O₅, and SnO₂; and the narrower bandgap semiconductor material has a bandgap E_(g)<1.0 eV and is selected from the group consisting of: PbS, InP, InAs, CdS, CdSe, CdTe, Bi₂S₃, and AlSb.

Another aspect of the present invention is an improved quantum dot (QD) sensitized wide bandgap (WBG) semiconductor heterojunction photovoltaic (PV) device, comprising:

-   -   (a) an electron conductive layer;     -   (b) an active photovoltaic (PV) layer adjacent the electron         conductive layer;     -   (c) a hole conductive layer adjacent the active PV layer; and     -   (d) an electrode layer adjacent the hole conductive layer;         wherein the active PV layer comprises:         -   (i) a wide bandgap (WBG) semiconductor material with             E_(g)≧2.0 eV, in the form of a 2-dimensional matrix defining             at least two open spaces; and         -   (ii) a narrower bandgap semiconductor material with             E_(g)<2.0 eV, in the form of quantum dots (QD's) filling the             open spaces defined by the matrix of WBG semiconductor             material and establishing a heterojunction therewith.

In accordance with embodiments of the present invention, the QD's constitute from about 40 to about 90 vol. % of the active PV layer, typically about 70 vol. % of the active PV layer; each QD is columnar- or grain-shaped and extends from the electron conductive layer to the hole conductive layer; the WBG and narrower bandgap semiconductor materials are immiscible; and each QD is isolated by the matrix of WBG semiconductor material.

According to the present invention, each columnar- or grain-shaped QD has a physical dimension within the range from about 2 to about 10 nm for exhibiting quantum containment effects; and the active PV layer is from about 2 to about 20 nm thick, preferably from about 2 to about 10 nm thick.

Preferably, the WBG semiconductor material has a bandgap E_(g)≧3.0 eV; and the narrower bandgap semiconductor material has a bandgap E_(g)<1.0 eV.

According to embodiments of the present invention, the WBG semiconductor material is an electron conductive material selected from the group consisting of: TiO₂, ZnS, ZnO, Ta₂O₅, Nb₂O₅, and SnO₂; and the narrower bandgap semiconductor material is selected from the group consisting of: PbS, InP, InAs, CdS, CdSe, CdTe, Bi₂S₃, and AlSb. Preferably, the WBG semiconductor material is anatase TiO₂; and the narrower bandgap semiconductor material is PbS.

In accordance with embodiments of the present invention, the electron conductive layer is comprised of an n-type semiconductor material, and is preferably transparent and formed over a surface of a transparent substrate.

According to preferred embodiments of the present invention, the n-type semiconductor material comprises a layer of a transparent conductive oxide (TCO) material selected from the group consisting of: SnO₂:F, ZnO, SrRuO₃, In₂O₃—SnO₂ (ITO), and CdSnO₄, the layer comprising a granular, nano-textured surface in direct, preferably epitaxial, contact with the active PV layer.

In accordance with embodiments of the present invention, adhesion and seed layers are present intermediate the surface of the transparent substrate and the TCO layer; the adhesion layer comprising at least one material selected from the group consisting of: Ti, Ta, CrTa, and CrTi; and the seed layer comprising at least one material selected from the group consisting of: Al, Au, Ag, Pt, Pd, Cu, Ni, Rh, Ru, Co, Re, and Ti. Preferably, the adhesion layer comprises Ti and the seed layer comprises Au.

According to embodiments of the present invention, the hole conductive layer comprises a semiconductor material (“SC”) wherein (Φ_(A)-VB)_(SC)>(Φ_(A)-VB)_(QD), e.g., Si, p-Si, GaAs, or p-GaAs; and the electrode layer is comprised of an electrically conductive material selected from the group consisting of: Hf, Au, Ni, Al, Cu, Pt, Pd, and TCO materials. Preferably, each of the electron conductive and electrode layers is light transmissive, whereby the device is operable via irradiation of either or both light transmissive layers.

In accordance with embodiments of the present invention, the device further comprises:

-   -   (e) electrical contacts to each of the electron conductive and         electrode layers.

Another aspect of the present invention is an improved method of fabricating a quantum dot (QD) sensitized wide bandgap (WBG) semiconductor heterojunction photovoltaic (PV) device, comprising steps of:

-   -   (a) providing an electron conductive layer;     -   (b) forming an active photovoltaic (PV) layer in contact with         the electron conductive layer;     -   (c) forming a hole conductive layer in contact with the active         PV layer; and     -   (d) forming an electrode layer in contact with the hole         conductive layer;     -   wherein step (b) comprises:         -   (i) providing a wide bandgap (WBG) semiconductor material             with E_(g)≧2.0 eV;         -   (ii) providing a narrower bandgap semiconductor material             with E_(g)<2.0 eV; and         -   (iii) forming a 2-dimensional matrix comprising the WBG             material, the matrix defining a plurality of open spaces;             and         -   (iv) filling the open spaces defined by said matrix of WBG             semiconductor material with quantum dots (QD's) of the             narrower bandgap semiconductor material, the narrower             bandgap and WBG semiconductor materials forming a             heterojunction therebetween.

In accordance with embodiments of the present invention, steps (b)(iii) and (b)(iv) occur substantially simultaneously and each comprise a physical vapor deposition (PVD) process. Preferably, steps (b)(iii) and (b)(iv) are performed substantially simultaneously by co-sputter deposition of the narrower bandgap and WBG semiconductor materials.

According to preferred embodiments of the present invention, steps (b)(iii) and (b)(iv) are performed according to process conditions typical of Zone 1 of a Thornton diagram and include low to moderate substrate temperatures of about 200° C. and relatively high sputter gas pressures >20 mTorr of inert gas. Steps (b)(iii) and (b)(iv) may further comprise addition of at least one gas comprising at least one constituent element of the narrower bandgap and WBG semiconductor materials.

In accordance with embodiments of the present invention, the QD's constitute from about 40 to about 90 vol. % of the active PV layer formed in step (b), typically about 70 vol. %.

Preferably, steps (b)(i) and (b)(ii) comprise providing immiscible WBG and narrower bandgap semiconductor materials; steps (b)(iii) and (b)(iv) form columnar- or grain-shaped QD's which extend from the electron conductive layer to the hole conductive layer, each QD being isolated by the matrix of WBG semiconductor material; and each columnar- or grain-shaped QD formed in steps (b)(iii) and (b)(iv) has a physical dimension within the range from about 2 to about 10 nm for exhibiting quantum containment effects.

According to embodiments of the present invention, the active PV layer formed in steps (b)(iii) and (b)(iv) is from about 2 to about 20 nm thick, preferably from about 2 to about 10 nm thick; step (b)(i) preferably comprises providing a WBG semiconductor material having a bandgap E_(g)≧3.0 eV; and step (b)(ii) preferably comprises providing a narrower bandgap semiconductor material having a bandgap E_(g)<1.0 eV.

Embodiments of the present invention include those wherein step (b)(i) comprises providing a WBG semiconductor material as an electron conductive material selected from the group consisting of: TiO₂, ZnS, ZnO, Ta₂O₅, Nb₂O₅, and SnO₂; and step (b)(ii) comprises providing a narrower bandgap semiconductor material selected from the group consisting of: PbS, InP, InAs, CdS, CdSe, CdTe, Bi₂S₃, and AlSb. Preferably, step (b)(i) comprises providing anatase TiO₂ as the WBG semiconductor material; and step (b)(ii) comprises providing PbS as the narrower bandgap semiconductor material.

In accordance with embodiments of the present invention, step (a) comprises providing an electron conductive layer comprised of an n-type semiconductor material. Preferably, step (a) comprises providing a transparent n-type semiconductor layer formed over a surface of a transparent substrate. E.g., step (a) comprises providing the n-type semiconductor material as a layer of a transparent conductive oxide (TCO) material selected from the group consisting of: SnO₂:F, ZnO, SrRuO₃, In₂O₃—SnO₂ (ITO), and CdSnO₄, wherein step (a) comprises providing the layer of TCO material with a granular, nano-textured surface; and step (b) comprises forming the active PV layer in direct contact with the layer of TCO material. Preferably, the interface between the active PV layer and the layer of TCO material is epitaxial.

Preferably, step (a) comprises forming the layer of TCO material by means of a 2-stage sputter deposition process comprising a first stage utilizing a low pressure sputtering atmosphere from about 1 to about 10 mTorr for deposition of an initial 2-90 nm thickness of the TCO layer, and a second stage utilizing a higher pressure sputtering atmosphere from about 10 to about 200 mTorr for deposition of the final 1-10 nm thickness of the TCO layer.

According to embodiments of the present invention, step (a) further comprises providing adhesion and seed layers intermediate the surface of the transparent substrate and the layer of TCO material; the adhesion layer comprises at least one material selected from the group consisting of: Ti, Ta, CrTa, and CrTi; and the seed layer comprises at least one material selected from the group consisting of: Al, Au, Ag, Pt, Pd, Cu, Ni, Rh, Ru, Co, Re, and Ti. Preferably, the adhesion layer comprises Ti and the seed layer comprises Au.

In accordance with embodiments of the present invention, step (c) comprises providing a hole conductive layer comprised of a semiconductor material (“SC”), wherein (Φ_(A)-VB)_(SC)>(Φ_(A)-VB)_(QD), e.g., Si, p-Si, GaAs, or p-GaAs; and step (d) comprises providing an electrode comprised of an electrically conductive material selected from the group consisting of: Hf, Au, Ni, Al, Cu, Pt, Pd, and TCO materials.

Preferably, the electron conductive layer provided in step (a) and the electrode layer formed in step (d) are each light transmissive, whereby the device is operable via irradiation of either or both light transmissive layers.

According to embodiments of the present invention, the method further comprises:

-   -   (e) a step of forming electrical contacts to each of the         electron conductive and electrode layers.

Additional advantages and aspects of the present invention will become readily apparent to those skilled in the art from the following detailed description, wherein embodiments of the present invention are shown and described, simply by way of illustration of the best mode contemplated for practicing the present invention. As will be described, the present invention is capable of other and different embodiments, and its several details are susceptible of modification in various obvious respects, all without departing from the spirit of the present invention. Accordingly, the drawings and description are to be regarded as illustrative in nature, and not as limitative.

BRIEF DESCRIPTION OF THE DRAWINGS

The following detailed description of the embodiments of the present invention can best be understood when read in conjunction with the following drawings, in which the various features are not necessarily drawn to scale but rather are drawn as to best illustrate the pertinent features, wherein:

FIG. 1 is a band diagram schematically illustrating a solid-state heterojunction QD-sensitized PV cell;

FIG. 2 is a band diagram schematically illustrating exciton generation in QD's via impact ionization (inverse Auger effect);

FIG. 3 is a band diagram schematically illustrating exciton generation in a solid-state heterojunction QD-sensitized PV cell;

FIGS. 4(A) and 4(B) schematically illustrate the directions of electron and hole travel, respectively, in the QD-sensitized PV cell of FIG. 3;

FIG. 5 is a simplified, schematic cross-sectional view of an illustrative, but non-limitative, embodiment of a solid-state heterojunction QD-sensitized PV cell according to the present invention;

FIG. 6 is a simplified, schematic plan view of 2-dimensional honeycomb-type structure of the active PV layer of QD-sensitized PV cells according to the present invention;

FIG. 7 is a Thornton-type diagram illustrating various crystallographic structures/morphologies of films obtainable as a function of deposition parameters; and

FIGS. 8(A) and 8(B) schematically illustrate the impact ionization/inverse Auger process and 2-sided irradiation capability of QD-sensitized PV cells according to the present invention.

DESCRIPTION OF THE INVENTION

The present invention is based upon recognition that solid-state heterojunction QD-sensitized PV cells can be fabricated with substantially improved viability when used as solar energy-to-electrical energy conversion devices than heretofore possible via conventional methodologies, including absorption of the QD material from colloidal solution and in situ processing. According to the present invention, the active photovoltaic layer of solid-state heterojunction QD-sensitized PV cells is a novel granular film structure comprising a columnar-shaped, 2-dimensional matrix including a substantially greater volume (hence amount) of QD material, relative to WBG material, than heretofore afforded by the aforementioned conventional methodologies, such as absorption of QD material from solution and in situ processing.

More specifically, according to the present invention, a substrate (preferably transparent) with an electrically conductive granular layer thereon (e.g., transparent conductive oxide, “TCO”, such as an indium-tin oxide, “ITO”, layer) having peaks and valleys and a desired crystallographic orientation is provided in an initial step, and in a subsequent step an active photovoltaic (“PV”) layer comprising QD and WBG material is co-deposited thereon, e.g., by a physical vapor deposition (PVD) process such as sputtering. The QD's nucleate as precipitates filling the spaces in the 2-dimensional matrix of WBG material, with the volume fraction of the QD material in the active PV layer being in the range from about 40 to about 90 vol. %, typically about 70 vol. %.

According to the invention, the QD material is co-deposited with the immiscible WBG material, e.g., by sputter deposition utilizing separate targets or a composite target comprised of both materials, such that the QD material nucleates as a precipitate at the peaks of the electrically conductive ITO layer and forms columns (or grains) extending substantially orthogonally therefrom to a hole conductive layer, whereas the WBG material migrates to and segregates at the boundaries between adjacent columns (grains) of QD material. A film structure wherein QD material fills the spaces defined by a 2-dimensional matrix of WBG semiconductor material as a grain boundary segregant is thus formed, wherein the QD material occupies as much as 90 vol. % of the resultant film. The particles (columns) of QD material are well isolated, with dimensions in the nm range, i.e., consistent with the requirements for quantum confinement. The result is an active PV layer comprising a QD-sensitized WBG semiconductor material, including a sufficiently large area of QD-WBG contact, thereby well-suited for obtaining devices with enhanced PV conversion efficiencies via impact ionization (inverse Auger recombination), as described above.

Referring now to FIG. 5, shown therein is a simplified, schematic cross-sectional view of an illustrative, but non-limitative, embodiment of a solid-state heterojunction QD-sensitized PV cell 10 according to the present invention. As shown, cell 10 comprises a stacked layer structure including, in sequence: a (preferably transparent) substrate 1, an adhesion/seed layer 2A/2B, an electron conductive layer 3, an active PV layer 4, a hole conductive layer 5, and a (preferably transparent) electrode 6. Electrical contacts 7 and 8 to the electron conductive and electrode layers 3 and 6, respectively, provide electrical outputs for connection to a load device 9.

An illustrative, but non-limitative, sequence of process steps for fabricating cell 10 via PVD processing, e.g., co-sputtering, is described in detail in the following:

In an initial step, a substrate 1 is provided, comprising a material selected from the group consisting of glass, metals, alloys, polymers, ceramics, and composites and laminates thereof, with glass or other transparent material being preferred for facilitating irradiation of the active PV layer. A thin adhesion layer 2A, i.e., ˜2 nm thick, of at least one material selected from the group consisting of Ti, Ta, CrTa, and CrTi is formed on the surface of the substrate 1, it generally being advantageous to form the adhesion layer 2A under deposition conditions yielding a smooth finished surface, e.g., a regime utilizing a low pressure sputtering atmosphere, such as from about 1 to about 5 mTorr Ar, Kr, or Xe. A seed layer 2B from about 1 to about 5 nm thick and comprising at least one material selected from the group consisting of Al, Au, Ag, Pt, Pd, Cu, Ni, Rh, Ru, Co, Re, and Ti is then formed under similar conditions in overlying contact with the adhesion layer 2A. The seed layer 2B functions to provide a desired crystallographic texture and adequate lattice match to subsequently deposited overlying layers. Suitable alternative materials for the seed layer 2B include alloy compositions primarily comprising fcc or hcp metals with additions of other fcc or hcp metals or even bcc materials. A preferred adhesion layer/seed layer 2A/2B combination is Ti/Au.

In the next step according to the inventive methodology, a first electrode 3 comprised of a transparent electrically conductive material, e.g., a transparent conductive oxide (“TCO”) such as SnO₂:F, ZnO, SrRuO₃, In₂O₃—SnO₂ (“ITO”), and CdSnO₄, is formed on the adhesion layer/seed layer 2A/2B in a 2-stage sputtering process. A low pressure sputtering atmosphere, e.g., from about 1 to about 10 mTorr, is utilized in the first stage for deposition of the initial 2-90 nm thickness of the TCO, and a higher pressure sputtering atmosphere, e.g., from about 10 to about 200 mTorr, is utilized in the second stage for deposition of the final 1-10 nm thickness of the TCO. The 2-stage sputtering process creates a granular, nano-textured TCO surface necessary for achieving 2-12 nm separation of the subsequently deposited QD columns or grains in the overlying active PV layer.

According to the next step of the inventive methodology, the active PV layer 4 comprised of a WBG semiconductor material (i.e., ≧2.0 eV, preferably ≧3.0 eV), and a narrower bandgap QD semiconductor material (i.e., <2.0 eV, preferably <1.0 eV) is deposited on the granular, nano-textured surface of the TCO layer 3 via a PVD process, preferably a co-sputter deposition process utilizing separate targets or targets comprised of mixtures or segments of each material, and DC, AC, or RF plasma generation. Depending upon the electrical characteristics of the particular targets employed for the co-deposition process, DC- or RF-magnetron or DC- or RF-diode cathodes may be utilized. Suitable materials for use as the WBG semiconductor include electron conductive materials such as TiO₂, ZnS, ZnO, Ta₂O₅, Nb₂O₅, and SnO₂, with anatase TiO₂ being preferred; and suitable materials for use as the QD material include PbS, InP, InAs, CdS, CdSe, CdTe, Bi₂S₃, and AlSb, with PbS being preferred. The QD material is co-deposited with the immiscible WBG material, such that the QD material nucleates at the peaks of the TCO layer 3 and forms columns (or grains) extending substantially orthogonally therefrom, whereas the WBG material migrates to and segregates at the boundaries between adjacent columns (grains) of QD material to form a 2-dimensional matrix, as for example, the substantially honeycomb-shaped matrix schematically shown in plan view in FIG. 6, in which the QD material fills the spaces of the 2-dimensional matrix formed by the WBG semiconductor material and establishes a heterojunction therewith.

The sputter deposition parameters utilized for the co-deposition process are similar to the deposition parameters utilized for the second deposition phase of the TCO layer 3 (described supra), and are similar to those utilized for forming the sharply separated columnar grains in Zone 1 of a Thornton diagram (see, e.g., J. Vac. Sci. Technol. 11, 666-670 (1974) or U.S. Pat. No. 4,557,981). In contrast with QD-WBG active layers produced by conventional methodologies, an active PV layer 4 comprising a 2-dimensional matrix of QD material with WBG material as a grain boundary segregant is formed according to the invention, wherein the QD material constitutes a substantially increased portion of the volume of the active PV layer 4, i.e., from about 40 to about 90 vol. % of the resultant film, typically about 70 vol. %.

Process conditions typical of Zone 1 of the Thornton diagram include low to moderate substrate temperature, e.g., <40% homologous temperature (defined as T_(substrate)/T_(melting)), preferably about 200° C., and relatively high sputter gas pressures >20 mTorr of inert gas (e.g., Ar), preferably >30 mTorr. This combination of process parameters yields thin films with columnar (or granular) grain structures with varying amounts of porosity between neighboring grains, and is ideal for facilitating segregation of immiscible materials, since the columnar grain structures form the QD's while the immiscible WBG material is accumulated/trapped at the porous grain boundaries. The resultant structure may resemble a honeycomb when viewed in plan view (as in FIG. 6), where the WBG semiconductor material forms a 2-dimensional, substantially honeycomb-shaped matrix or lattice and the QD semiconductor material (shaded in the figure) occupies the spaces defined by the matrix or lattice.

The particles (columns) of QD material are well isolated, with dimensions in the nm range, consistent with the requirements for quantum confinement. Also in contrast with conventional QD-WBG active layer materials and QD-WBG PV cells, the columnar-shaped grains extend for substantially the entire thickness of the active PV layer 4, and contact the electron conductive layer 3 and the subsequently formed hole conductive layer 5.

Proper adjustment of the constituent stoichiometries of the WBG matrix (segregant) material, e.g., Ti and O₂ of TiO₂, and QD columnar material, e.g., Pb and S of PbS, may require addition of gases such as H₂S and/or O₂ during the co-deposition process. Anatase TiO₂ is a preferable matrix material (segregant) in view of its ability to accept charge injection from the neighboring QD material at the grain boundaries. In addition, it is immiscible in the material of the QD, e.g., PbS, and therefore drifts along the growing surfaces of the QD columns or grains until captured in the physically recessed regions of the grain boundaries. Simultaneously, the QD semiconductor material forms an epitaxial interface with the TCO layer 3, e.g., ITO. The co-deposition process therefore leads to isolated QD semiconductor columns or grains with physical dimension consistent with obtaining/exhibiting quantum confinement effects, i.e., from about 2 to about 10 nm. A log-normal distribution of grain diameters, d, occurs, and with optimization of co-deposition parameters σ_(d)/d is less than ˜20%. Suitable thicknesses of the QD-WBG active PV layer according to the invention range from about 2 to about 20 nm, with from about 2 to about 10 nm preferred.

In the next step according to the inventive methodology, a hole conductive semiconductor layer 5 is deposited on the active PV layer 4 via a sputtering process performed under conditions similar to those utilized for deposition of the seed layer 2B. In this regard, inorganic semiconductor (SC) materials wherein (Φ_(A)-VB)_(SC)>(Φ_(A)-VB)_(QD), e.g., Si, p-Si, GaAs, or p-GaAs, are preferred, inasmuch as they are capable of accepting holes from the QD (absorber) as well as injecting electrons from the contact back into the QD. The hole conductor layer 5 is from about 1 to about 20 nm thick and is optimized for maximum hole conductivity and minimum electron tunneling current. The thickness of the hole conductor layer is desirably minimized in order to achieve transparency, thereby facilitating exposure of either side of the device to light and use as an electricity generating window covering.

An electrode layer 6 is then formed over the hole conductor layer, and may comprise a relatively thin metal layer, i.e., from about 2 to about 20 nm thick and comprised of, e.g., Hf, Au, Ni, Al, Cu, Pt, or Pd, or a relatively thick TCO layer, i.e., from about 10 to about 100 nm thick, and comprised of ITO. Process conditions for forming the second electrode layer 6 are not critical, and the latter may, if desired or necessary for protection from deleterious environmental effects, be covered with a relatively thick, impervious layer of a transparent glass or polymeric material.

Finally, respective electrical output contacts 7 and 8 are affixed to the electron conductive layer 3 and electrode layer 6 in conventional manner in order to obtain electrical output from the cell for supply to a load 9.

An advantage of the present invention is the ability to fabricate cells from optically transparent substrate, adhesion/seed layer, electron conductor, and electrode materials, whereby irradiation of either or both sides is possible. Referring to FIGS. 8(A) and 8(B), schematically illustrated therein are the impact ionization/inverse Auger recombination process and 2-sided irradiation capability of solid-state heterojunction QD-sensitized PV cells according to the present invention.

The present invention therefore advantageously provides improved, high photon conversion efficiency, solid-state heterojunction, quantum dot-sensitized wide bandgap (QD-WBG) photovoltaic (PV) devices which avoid the above-described limitations imposed on the quantum (photon conversion) efficiency of prior QD-WBG devices fabricated according to conventional methodologies. The QD-WBG PV devices of the present invention are especially useful when utilized as solar cells for the direct conversion of solar radiation to electricity. Further, QD-WBG PV devices according to the present invention can be fabricated in cost-effective manner utilizing well-known PVD techniques such as sputter deposition.

In the previous description, numerous specific details are set forth, such as specific materials, structures, processes, etc., in order to provide a better understanding of the present invention. However, the present invention can be practiced without resorting to the details specifically set forth. In other instances, well-known processing materials and techniques have not been described in detail in order not to unnecessarily obscure the present invention.

Only the preferred embodiments of the present invention and but a few examples of its versatility are shown and described in the present disclosure. It is to be understood that the present invention is capable of use in various other combinations and environments and is susceptible of changes and/or modifications within the scope of the inventive concept as expressed herein. 

1. A quantum dot (QD) sensitized wide bandgap (WBG) semiconductor heterojunction photovoltaic (PV) device, including an active photovoltaic (PV) layer comprising: a wide bandgap (WBG) semiconductor material with E_(g)≧2.0 eV, in the form of a 2-dimensional matrix defining at least two open spaces; and a narrower bandgap semiconductor material with E_(g)<2.0 eV, in the form of quantum dots (QD's) filling said open spaces defined by said matrix of WBG semiconductor material and establishing a heterojunction therewith.
 2. The device of claim 1, further comprising: an electron conductive layer adjacent a first side of said active PV layer; a hole conductive layer adjacent a second side of said active PV layer; and an electrode layer adjacent said hole conductive layer.
 3. The device of claim 2, wherein: each QD is columnar- or grain-shaped and extends from said electron conductive layer to said hole conductive layer; said WBG and narrower bandgap semiconductor materials are immiscible; and each QD is isolated by said matrix of WBG semiconductor material.
 4. The device of claim 1, wherein: said WBG semiconductor material has a bandgap E_(g)≧3.0 eV and is an electron conductive material selected from the group consisting of: TiO₂, ZnS, ZnO, Ta₂O₅, Nb₂O₅, and SnO₂; and said narrower bandgap semiconductor material has a bandgap E_(g)<1.0 eV and is selected from the group consisting of: PbS, InP, InAs, CdS, CdSe, CdTe, Bi₂S₃, and AlSb.
 5. A quantum dot (QD) sensitized wide bandgap (WBG) semiconductor heterojunction photovoltaic (PV) device, comprising: (a) an electron conductive layer; (b) an active photovoltaic (PV) layer in contact with said electron conductive layer; (c) a hole conductive layer in contact with said active PV layer; and (d) an electrode layer in contact with said hole conductive layer; wherein said active PV layer comprises: (i) a wide bandgap (WBG) semiconductor material with E_(g)>2.0 eV, in the form of a 2-dimensional matrix defining a plurality of open spaces; and (ii) a narrower bandgap semiconductor material with E_(g)<2.0 eV, in the form of quantum dots (QD's) filling said open spaces defined by said matrix of WBG semiconductor material and establishing a heterojunction therewith.
 6. The device of claim 5, wherein: said QD's constitute from about 40 to about 90 vol. % of said active PV layer.
 7. The device of claim 6, wherein: said QD's constitute about 70 vol. % of said active PV layer.
 8. The device of claim 5, wherein: (i) each QD is columnar- or grain-shaped and extends from said electron conductive layer to said hole conductive layer; (ii) said WBG and narrower bandgap semiconductor materials are immiscible; and (iii) each QD is isolated by said matrix of WBG semiconductor material.
 9. The device of claim 8, wherein: each said columnar- or grain-shaped QD has a physical dimension within the range from about 2 to about 10 nm for exhibiting quantum containment effects.
 10. The device of claim 8, wherein: said active PV layer is from about 2 to about 20 nm thick.
 11. The device of claim 10, wherein: said active PV layer is from about 2 to about 10 nm thick.
 12. The device of claim 5, wherein: (i) said WBG semiconductor material has a bandgap E_(g)≧3.0 eV; and (ii) said narrower bandgap semiconductor material has a bandgap E_(g)<1.0 eV.
 13. The device of claim 5, wherein: (i) said WBG semiconductor material is an electron conductive material selected from the group consisting of: TiO₂, ZnS, ZnO, Ta₂O₅, Nb₂O₅, and SnO₂; and (ii) said narrower bandgap semiconductor material is selected from the group consisting of: PbS, InP, InAs, CdS, CdSe, CdTe, Bi₂S₃, and AlSb.
 14. The device of claim 13, wherein: (i) said WBG semiconductor material is anatase TiO₂; and (ii) said narrower bandgap semiconductor material is PbS.
 15. The device of claim 5, wherein: said electron conductive layer is comprised of a layer of an n-type semiconductor material.
 16. The device of claim 15, wherein: said n-type semiconductor layer is transparent and is formed over a surface of a transparent substrate.
 17. The device of claim 16, wherein: said n-type semiconductor layer comprises a layer of a transparent conductive oxide (TCO) material selected from the group consisting of: SnO₂:F, ZnO, SrRuOs, In₂O₃—SnO₂ (ITO), and CdSnO₄.
 18. The device of claim 17, wherein: said TCO layer comprises a granular, nano-textured surface in direct contact with said active PV layer.
 19. The device of claim 18, wherein: an interface between said TCO layer and said active PV layer is epitaxial.
 20. The device of claim 18, further comprising: adhesion and seed layers intermediate said surface of said transparent substrate and said TCO layer.
 21. The device of claim 20, wherein: (i) said adhesion layer comprises at least one material selected from the group consisting of: Ti, Ta, CrTa, and CrTi; and (ii) said seed layer comprises at least one material selected from the group consisting of: Al, Au, Ag, Pt, Pd, Cu, Ni, Rh, Ru, Co, Re, and Ti.
 22. The device of claim 21, wherein: (i) said adhesion layer comprises Ti; and (ii) said seed layer comprises Au.
 23. The device of claim 5, wherein: said hole conductive layer comprises a semiconductor material.
 24. The device of claim 23, wherein: said hole conductive layer comprises Si, p-Si, GaAs, or p-GaAs.
 25. The device of claim 5, wherein: said electrode is comprised of an electrically conductive material selected from the group consisting of: Hf, Au, Ni, Al, Cu, Pt, Pd, and TCO materials.
 26. The device of claim 5, wherein: each of said electron conductive and electrode layers is light transmissive, whereby said device is operable via irradiation of either or both said light transmissive layers.
 27. The device of claim 5, further comprising: (e) electrical contacts to each of said electron conductive and electrode layers.
 28. A method of fabricating a quantum dot (QD) sensitized wide bandgap (WBG) semiconductor heterojunction photovoltaic (PV) device, comprising steps of: (a) providing an electron conductive layer; (b) forming an active photovoltaic (PV) layer in contact with said electron conductive layer; (c) forming a hole conductive layer in contact with said active PV layer; and (d) forming an electrode layer in contact with said hole conductive layer; wherein step (b) comprises: (i) providing a wide bandgap (WBG) semiconductor material with E_(g)≧2.0 eV; (ii) providing a narrower bandgap semiconductor material with E_(g)<2.0 eV; and (iii) forming a 2-dimensional matrix comprising said WBG material, said matrix defining a plurality of open spaces; and (iv) filling said open spaces defined by said matrix of WBG semiconductor material with quantum dots (QD's) of said narrower bandgap semiconductor material, said narrower bandgap and WBG semiconductor materials forming a heterojunction therebetween.
 29. The method according to claim 28, wherein: steps (b)(iii) and (b)(iv) occur substantially simultaneously.
 30. The method according to claim 29, wherein: steps (b)(iii) and (b)(iv) each comprise a physical vapor deposition (PVD) process.
 31. The method according to claim 30, wherein: steps (b)(iii) and (b)(iv) are performed substantially simultaneously by co-sputter deposition of said narrower bandgap and WBG semiconductor materials.
 32. The method according to claim 31, wherein: steps (b)(iii) and (b)(iv) are performed according to process conditions typical of Zone 1 of a Thornton diagram and include low to moderate substrate temperatures of about 200° C. and relatively high sputter gas pressures >20 mTorr of inert gas.
 33. The method according to claim 32, wherein: steps (b)(iii) and (b)(iv) further comprise addition of at least one gas comprising at least one constituent element of said narrower bandgap and WBG semiconductor materials.
 34. The method according to claim 28, wherein: said QD's constitute from about 40 to about 90 vol. % of said active PV layer formed in step (b).
 35. The method according to claim 34, wherein: said QD's constitute about 70 vol. % of said active PV layer formed in step (b).
 36. The method according to claim 28, wherein: steps (b)(i) and (b)(ii) comprise providing immiscible WBG and narrower bandgap semiconductor materials; and steps (b)(iii) and (b)(iv) form columnar- or grain-shaped QD's which extend from said electron conductive layer to said hole conductive layer, each QD being isolated by said matrix of WBG semiconductor material.
 37. The method according to claim 36, wherein: each said columnar- or grain-shaped QD formed in steps (b)(iii) and (b)(iv) has a physical dimension within the range from about 2 to about 10 nm for exhibiting quantum containment effects.
 38. The method according to claim 36, wherein: said active PV layer formed in steps (b)(iii) and (b)(iv) is from about 2 to about 20 nm thick.
 39. The method according to claim 38, wherein: said active PV layer formed in steps (b)(iii) and (b)(iv) is from about 2 to about 10 nm thick.
 40. The method according to claim 28, wherein: step (b)(i) comprises providing a WBG semiconductor material having a bandgap E_(g)≧3.0 eV; and step (b)(ii) comprises providing a narrower bandgap semiconductor material having a bandgap E_(g)<1.0 eV.
 41. The method according to claim 28, wherein: step (b)(i) comprises providing a WBG semiconductor material as an electron conductive material selected from the group consisting of: TiO₂, ZnS, ZnO, Ta₂O₅, Nb₂O₅, and SnO₂; and step (b)(ii) comprises providing a narrower bandgap semiconductor material selected from the group consisting of: PbS, InP, InAs, CdS, CdSe, CdTe, Bi₂S₃, and AlSb.
 42. The method according to claim 41, wherein: step (b)(i) comprises providing anatase TiO₂ as said WBG semiconductor material; and step (b)(ii) comprises providing PbS as said narrower bandgap semiconductor material.
 43. The method according to claim 28, wherein: step (a) comprises providing an electron conductive layer comprised of an n-type semiconductor material.
 44. The method according to claim 43, wherein: step (a) comprises providing a transparent n-type semiconductor layer formed over a surface of a transparent substrate, said transparent n-type semiconductor layer comprising a layer of a transparent conductive oxide (TCO) material selected from the group consisting of: SnO₂:F, ZnO, SrRuO₃, In₂O₃—SnO₂ (ITO), and CdSnO₄.
 45. The method according to claim 44, wherein: step (a) comprises providing said layer of TCO material with a granular, nano-textured surface; and step (b) comprises forming said active PV layer in direct contact with said layer of TCO material.
 46. The method according to claim 45, wherein: step (b) comprises forming said active PV layer with an epitaxial interface with said layer of TCO material.
 47. The method according to claim 46, wherein: step (a) comprises forming said layer of TCO material by means of a 2-stage sputter deposition process comprising a first stage utilizing a low pressure sputtering atmosphere from about 1 to about 10 mTorr for deposition of an initial 2-90 nm thickness of said TCO layer, and a second stage utilizing a higher pressure sputtering atmosphere from about 10 to about 200 mTorr for deposition of the final 1-10 nm thickness of said TCO layer.
 48. The method according to claim 44, wherein: step (a) further comprises providing adhesion and seed layers intermediate said surface of said transparent substrate and said layer of TCO material, said adhesion layer comprising at least one material selected from the group consisting of: Ti, Ta, CrTa, and CrTi; and said seed layer comprising at least one material selected from the group consisting of: Al, Au, Ag, Pt, Pd, Cu, Ni, Rh, Ru, Co, Re, and Ti.
 49. The method according to claim 48, wherein: said adhesion layer comprises Ti; and said seed layer comprises Au.
 50. The method according to claim 28, wherein: step (c) comprises providing a hole conductive layer comprised of a semiconductor material.
 51. The method according to claim 50, wherein: step (c) comprises providing a hole conductive layer comprised of Si, p-Si, GaAs, or p-GaAs.
 52. The method according to claim 28, wherein: step (d) comprises providing an electrode comprised of an electrically conductive material selected from the group consisting of: Hf, Au, Ni, Al, Cu, Pt, Pd, and TCO materials.
 53. The method according to claim 28, wherein: said electron conductive provided in step (a) and said electrode layer formed in step (d) are each light transmissive, whereby said device is operable via irradiation of either or both said light transmissive layers.
 54. The method according to claim 28, further comprising: (e) forming electrical contacts to each of said electron conductive and electrode layers. 